Our Tungsten Carbide (WC) Crucibles are engineered for the most demanding thermal and mechanical environments. Unlike standard graphite or ceramic crucibles, WC crucibles offer unparalleled hardness 90-92HRA and density 14.5-15.0 g/cm. These are specifically designed for applications where contamination must be minimized and the container must withstand aggressive abrasive forces or high-vacuum induction heating.
| Property | Value / Specification |
| Material Composition | 90-94% WC + 6-10% Co(Cobalt Binder) |
| Density | 14.5-15.0g/cm |
| Hardness | 90-92HRA |
| Melting Point | 2870WC Base |
| Transverse Rupture Strength | 2600MPa |
| Surface Roughness | < 0.4 μ Polished |
We offer a range of standard cylindrical and tapered geometries. Additionally, we provide OEM Customization for:
Wall thickness (for specific thermal gradients).
Integrated lids and pouring spouts.
Threaded bases for planetary ball mill integration.
| Diameter(mm) | Thickness(mm) | Height(mm) | Surface finish | inner surface finish | inner bottom finish |
| 30-50 | 2-10 | ≤200 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 50-100 | 3-15 | ≤300 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 100-150 | 3-15 | ≤350 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 150-200 | 5-20 | ≤400 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 200-300 | 8-25 | ≤500 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 300-400 | 8-30 | ≤600 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 400-450 | 8-30 | ≤650 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 450-600 | 8-35 | ≤800 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
Metallurgy: High-frequency induction melting of rare earth metals and alloys.
Laboratory Analysis: Used as milling jars or vessels for preparing high-purity geological or ceramic samples.
Crystal Growth: Specialized containers for growing synthetic crystals under high pressure/temperature.
Thin Film Deposition: Evaporation sources for vacuum coating processes.
Чаро моро интихоб кунед:
1. Шумо метавонед маводи комилро мувофиқи талаботи худ бо нархи ҳадди ақалл дастрас кунед.
2. Мо инчунин Reworks, FOB, CFR, CIF ва нархҳои интиқоли хонаро пешниҳод менамоем. Мо ба шумо пешниҳод менамоем, ки барои интиқол, ки хеле сарфакор хоҳад буд, созед.
3. Маводҳое, ки мо пешниҳод мекунем, аз шаҳодатномаи санҷиши ашёи хом то изҳороти ниҳоии андозагирӣ комилан тафтишшаванда мебошанд. (Ҳисоботҳо мувофиқи талабот нишон дода мешаванд)
4. кафолат додани посух дар давоми 24 соат (одатан дар ҳамон соат)
5. Шумо метавонед алтернативаҳои саҳҳомӣ, таҳвили осиёбро бо кам кардани вақти истеҳсолӣ ба даст оред.
6. Мо пурра ба мизоҷони худ бахшидаем. Агар пас аз баррасии ҳама вариантҳо қонеъ кардани талаботи шумо имкон надиҳад, мо шуморо бо ваъдаҳои бардурӯғ, ки муносибатҳои хуби муштариёнро эҷод мекунанд, гумроҳ намекунем.
Намоиши завод
БО МО ТАМОС ГИРЕД
info@zztungsten.com